TWO PART LOW VISCOSITY
POLYURETHANE
CASTING RESIN
Kit consists of 125g of PART A
and 125g of PART B
FEATURES
Can be painted Very low viscosity Excellent fine detail reproduction Accepts high levels of mineral and metallic
fillers Suitable for casting into dental alginate Ultra low shrinkage Simple mix ratio of 100 : 100 by weight
ORIGINAL
UNFILLED
PART A is a black liquid and PART B is a clear liquid that react to form a black plastic. It has the strongest physical prosperities,
most heat resistance and the lowest viscosity similar to water. The cure is gradual
making the resin suitable for roto casting where the mould is slowly rotated as
the resin cures to form hollow objects. It doesn’t contain the filler that neutralizes Co2
gas created when the moisture in the air introduced when mixing reacts with the resin which can in certain circumstances form tiny bubbles.
ORIGINAL
FILLED
PART A is a black liquid and PART B is a clear liquid that react to form a black plastic. Similar to
the Low Odour resin but has marginally stronger physical properties, lower viscosity
and faster de-mould time. The cure is gradual making the resin suitable for
roto casting where the mould is slowly rotated as the resin cures to form
hollow objects. Contains a filler that helps minimize bubbles by absorbing Co2
gas produced when moisture in the air introduced when mixing the two parts
reacts with the resin.
LOW
ODOUR
PART A is a black liquid and PART B is a dark amber liquid that react to form a black plastic. Similar properties
to the Original Filled resin but has a different formula to give a low odour. The
cure profile makes the resin unsuitable for roto casting. Contains a filler that
helps minimize bubbles by absorbing Co2 gas produced when moisture in the air introduced
when mixing the two parts reacts with the resin.
FILLITE FILLER
Lightweight, hollow, spherical, low density, free-flowing, alumino-silicate
microspheres which when added at 50% of the weight of the resin will increase
the volume of the resin by 100-150% and remain pourable.
FUMED SILICA FILLER
Thixotropic additive, when added to the resin at 5% creates a paste that can be
brushed or spread into or on to moulds to create hollow casts.
METAL FILLERS FOR COLD CASTING
An initial layer of a resin and metal filler mix are applied to the surface of
the mould then the mould can be back filled with non metal filled resin. Once
cured the cast piece is carefully polished with fine wire wool to bring out the
finish of the metal. The higher the ratio of metal filler to resin used the
higher the quality of the finish.
A more efficient method if using a silicone mould is to cover the surface of
the mould in the powder, turn over and tap. A thin layer will stick to the
surface and the excess will fall off which can be collected and used
again. Very gently pour in the resin being careful not to disturb the
powder. The resin will soak into the powder leaving a very thin dense layer of
metal on the surface of the cast that can then be polished.
|