1. application examples:
By alloy with 17% chromium and 7% nickel, this material has a good
Corrosion resistance. This material is a high strength
Cold rolling achieved. Can a much higher compared to material 1.4301
Tensile strength until about 2000 N / mm sq are reached. This makes the material 1.4310
very well suited for stainless precision teaching tapes and protective films, as well as for
stainless steel springs and parts with higher strength.
Other application examples:
welded endless abrasive belts, conveyor belts
The material is in the standard DIN 17 224 1.4310 (new: DIN EN 10-151) as
Approved spring material.
For high demands on hardness and wear resistance, the grades should
1.4031 Mo (up to 0.80 mm thickness) or 1.4034 (from 1.0 to 3.0 mm thickness)
are.
2. labels:
German standard: 1.4310, X 10CrNi 17-7
AISI: 301
ASTM: S 30100
Also known as standard: 301S 21
Franz. Standard: Z 12 CN18-09
Japan. Standard: SUS 301
3. material composition: *.
C: 0,05 -0.15 %
SI: Max 2,00 0%
MN: Max 2.00%
P: Max 0.045%
S: max. 0.015%
CR: 16-19%
NI: 6 -9.5 %
Mon: Max 0.80%
exact composition can 2.2 or 3.1 in a factory certificate
(according to DIN
10 204) are documented for each batch.
4. delivery condition:
Structure: cold rolled (austenitic with shares in Umformmartensit), not
Hardenable surface: 2 H, roughness RA maximum 0,3 µm (printing the stripper)
Tensile strength: 1100 to 2000 N / mm²
The tensile strength can be by a tempering of steel at 330-370 ° C (about 4
Hours duration) to approximately 100-300 N / mm² (in relation to the original
Increase in strength of the material).
More mechanical and physical data: see sections 7 and 8.
5. tolerances:
Thickness tolerance: DIN EN 9445 table 1 or T3 (for grade 15-1700
N / mm²)
Width tolerance: ACC. to DIN EN 9445
Straightness: normal
6. mechanical details
Tensile yield strength RP 0.2: dependent on the tensile strength
Strain A-80: dependent on the tensile strength
After cutting (E.g. by tumbling) are good edge processing
following values possible:
Alternating bending (medium voltage = 0):
550 MPa (50% of the test samples are over 2 million cycles at normal
Environment), at a bend perpendicular to the direction of rolling.
Threshold tensile (minimum load = 0):
420 MPa (50% of the test samples are over 2 million cycles at normal
Environment), at a bend perpendicular to the rolling direction
Since the bending fatigue strength of various factors such as the
Depends on environmental conditions and the edge quality cannot
Values are guaranteed.
During heavy load or bends that are not perpendicular to the rolling direction,
requires the use of hardened steel as the material 1.4031 mo.
The highest application temperature is between 120 depending on the load and
250 ° C (cf. DIN 17224? Spring band made of stainless steel). Please note,
that the values for the modulus of elasticity with increasing temperature drop.
7. physical specifications:
Density: 7.9 g / cm³
Thermal conductivity: 15-19 W /(m °C) in dependence on the temperature
Heat capacity: 500 J / (kg ° C) average value at 50? 100 ° C
Thermal expansion: 15,5 x 10 -6 (between 30 - 100 ° C)
16.0 x 10 6 (between 30-200 ° C)
16.5 x 10 6 (between 30-300 ° C)
Electrical resistance: 0.73 ohm x mm sq/m
Elasticity mode: 185 000 MPa at 20 ° C
Relative permeability µr: maximum 24 (for more details see point 13)
More properties on request such as forming, welding, bending, etc.
Important note:
The information provided in this technical information sheet about the
Nature or use of the materials are used for description and are
no assurances.
The information, with whom we want to advise you, meet our experiences
and those of our suppliers. A liability for the results of
We cannot accept processing and application.
_____________________________________________________________________________________
In addition, in various strengths stock or procured:
for springs the materials:
- 1.1274 , 1.4031 Mo, 1.4310 , 1.4404 hard brass, bronze
for knives and tools:
hardened steels 1.2003 , 1.4034 and 1.2379
for heat-resistant parts (not in stock):
1.4767 and 1.4828
for corrosive environments:
Pure nickel, 1.4404
for parts with high conductivity:
SE-copper, Bronze, aluminum
Stainless Steel:
1.4301 (V2A)
for easy shim members:
1.0338 (DC04) or DC01
Titanium Grade 1 and Grade2:
Thickness/width/length of 0.5 mm to 3 mm / 1000 x 2000 mm
My articles is legally examined
Material | 1.4310 |
Material | CrNi-Stahl |
Material | Federstahl |
Material | 3D Drucker |
Material | Edelstahl |
Material | Rostfreies Edelstahl |
Stärke | 0,5mm |
Maßeinheit | m² |
Herstellernummer | 1.4310 200x200 |
Herstellungsland und -region | Deutschland |
Anzahl der Einheiten | 0,04 |