- Features:
- 1. High-efficiency adhesive-developed as an alternative to torch welding, it can repair metals and many other surfaces firmly and lastingly. It can bond almost all clean surfaces without dust and oil.
- 2. High temperature-can withstand temperatures up to 150°C. When fully cured, it is as hard as iron, and the bond line thickness is uniform.
- 3. Super bonding strength-it forms a strong and stable permanent bond, which should be used for many years. It can be shaped, tapped, filed, sanded and drilled according to the purpose.
- 4. Simple drying application program-preparation and application are simple and easy. Just mix, apply and let dry for a few hours. The full curing time is up to 24 hours.
- 5. Widely used-mainly used for casting steel, sand holes and holes, and filling cracks and other casting defects. It can be used to repair fuel tanks, pipelines, broken concrete, etc.
- Main Application:
- Used for casting metal repair. Made of epoxy resin, hardener, hardener, active diluent and various high-quality materials.
- Used for fast bonding of metal, glass, ceramics, plastics, wood, etc. Used for iron and steel castings, filled blisters, pores or cracks, casting defects, high curing
- Hardness, can be used at 100-150 C.
- Specifications:
- Overall performance:
- Gray muddy paste
B white pasta
- High strength, high temperature resistance, corrosion resistance, impact resistance, durability, simple operation
- Volume ratio: A: B = 1: 1
- Curing performance:
- Hardness: 80 (Shore-D)
- Shear strength: 18 (25 C)
- Full curing time: 12 hours (25 C)
- Bonding process:
- 1 First, make sure that the cleaning parts that need repair are free of stains.
- 2. Use files, sandpaper and other tools to process the plane.
- 3 Press the volume ratio of A and B components to 1:1 to evenly cover the object to be repaired.
- Notes:
- Remarks:
- The glue is mixed and used for about 1 hour. Must follow the ratio of A and B components
- Mix before use to avoid mixing any colors. With use, time runs out.
- Storage condition
- Stored in the temperature range of 15-28 C, the shelf life is 24 months.
- 24 hours after reaching the highest strength, shear strength> 20 mpa (200 kg / M2)