Loctite EA (Hysol) D609 Moisture & Chemical-Resistant 5-Min Seting Epoxy

LOCTITE EA (Hysol) D609 is an exceptional epoxy formulation recommended for lower temperature or wet industrial bonding applications where fast curing is required. This ultra clear, two part, low viscosity system mixes easily at room temperature. It is suitable for high performance structural bonding applications requiring a combination of very fast room temperature cure, low shrinkage, and excellent mechanical properties. Fully cured EA (Hysol) D609 is an excellent electrical insulator and provides superior resistance to vapors and gases, water, galvanic action, petroleum fuels, salt solution and many other organic and inorganic compounds. Recommended Substrates metals, phenolic plastics, polyester, glass and glass fabrics, hardboards and forestry products, ceramics, rubber, masonry materials and other construction materials. Features Very Fast Room Temperature No Solvents Easy to Mix Very Clear Self Leveling Data Sheets (Click on a link) TDS / Technical Data Sheet MSDS Parts A & B Typical Uncured Properties PartA PartB Mixed Pot Life @ 77°F, 20 grams mins -- -- 5 Color Clear Clear Clear Viscosity, cP 11,000 to 19,000 11,000 to 19,000 N/A MixRatio By weight 1 1 Byvolume 1 1 Typical Properties Typical Value Tensile Strength, psi, ASTM D 638 4200 Hardness, Shore D 75 Electrical Properties Typical Value Dielectric Strength, ASTM D149, V/mil 415 Shear Strength, psi, ASTM D 1002 Etched Aluminum Test Temp oF Typical Value 77 1800 Handling Mixing:Thisproductrequiresmixingtwocomponentstogetherjustpriortoapplication.Completemixingisnecessary.Thetemperatureoftheseparatecomponentspriortomixingisnotcritical,buttheyshouldbeclosetoroomtemperature. Application Bonding surfaces should be clean and dry.Once the adhesive is applied, the bonded parts should be held in contact until the part has developed handling strength. It is not necessary to clamp the parts unless movement during cure is likely. Mixing - Cartridges: Place cartridge in proper dispenser. To begin using a new cartridge, remove the cap and dispense a small amount of adhesive, making sure both parts A & B are extruding. Attach nozzle and dispense approximately 1-2" before applying onto the part to be bonded. Partially used cartridges should be stored with the mixing nozzle attached. To reuse, remove and discard the old nozzle, attach the new nozzle, and begin dispensing. Mixing - Bulk: Combine Part A (resin) and Part B (hardener) in the correct ratio (1:1) and mix thoroughly until the color and consistency are uniform. Ratios given above can be used for measuring larger amounts. Mixing the adhesive just prior to use is recommended. Heat buildup during or after mixing is normal. Do not mix quantities greater than 1/2 pound as dangerous heat buildup can occur causing uncontrolled decomposition of the mixed adhesive. Mixing smaller quantities will minimize the heat buildup. Cure Complete cure is obtained after 24 hours at 77°F. EA (Hysol) D609 will achieve handling strength after 10 minutes at 77°F (note: this can vary with different bond configurations). Clean Up It is important to remove excess adhesive from the work area and application equipment before it hardens. Many common solvents and citrus cleaners are suitable for removing uncured adhesive. Consult with your supplier's information pertaining to the safe and proper use of solvents. Packaging 50 ml EPS Cartridges 200 ml EPS Cartridges Gallon Systems Five Gallon Systems

Loctite EA (Hysol) D609 Moisture & Chemical-Resistant 5-Min Seting Epoxy

LOCTITE EA (Hysol) D609 is an exceptional epoxy formulation recommended for lower temperature or wet industrial bonding applications where fast curing is required. This ultra clear, two part, low viscosity system mixes easily at room temperature. It is suitable for high performance structural bonding applications requiring a combination of very fast room temperature cure, low shrinkage, and excellent mechanical properties. Fully cured EA (Hysol) D609 is an excellent electrical insulator and provides superior resistance to vapors and gases, water, galvanic action, petroleum fuels, salt solution and many other organic and inorganic compounds.

Recommended Substrates

metals, phenolic plastics, polyester, glass and glass fabrics, hardboards and forestry products, ceramics, rubber, masonry materials and other construction materials.

Features

Very Fast Room Temperature
No Solvents
Easy to Mix
Very Clear
Self Leveling

Data Sheets (Click on a link)

TDS / Technical Data Sheet

MSDS Parts A & B

Typical Uncured Properties	PartA	PartB	Mixed
Pot Life @ 77°F, 20 grams mins	--	--	5
Color	Clear	Clear	Clear
Viscosity, cP	11,000 to 19,000	11,000 to 19,000	N/A
MixRatio
By weight	1	1
Byvolume	1	1

Typical Properties	Typical Value
Tensile Strength, psi, ASTM D 638	4200
Hardness, Shore D	75

Electrical Properties	Typical Value
Dielectric Strength, ASTM D149, V/mil	415

Shear Strength, psi, ASTM D 1002 Etched Aluminum
Test Temp oF	Typical Value
77	1800

Handling

Mixing:Thisproductrequiresmixingtwocomponentstogetherjustpriortoapplication.Completemixingisnecessary.Thetemperatureoftheseparatecomponentspriortomixingisnotcritical,buttheyshouldbeclosetoroomtemperature.

Application

Bonding surfaces should be clean and dry.Once the adhesive is applied, the bonded parts should be held in contact until the part has developed handling strength. It is not necessary to clamp the parts unless movement during cure is likely.

Mixing - Cartridges: Place cartridge in proper dispenser. To begin using a new cartridge, remove the cap and dispense a small amount of adhesive, making sure both parts A & B are extruding. Attach nozzle and dispense approximately 1-2" before applying onto the part to be bonded. Partially uséd cartridges should be stored with the mixing nozzle attached. To reuse, remove and discard the old nozzle, attach the new nozzle, and begin dispensing.

Mixing - Bulk: Combine Part A (resin) and Part B (hardener) in the correct ratio (1:1) and mix thoroughly until the color and consistency are uniform. Ratios given above can be uséd for measuring larger amounts. Mixing the adhesive just prior to use is recommended. Heat buildup during or after mixing is normal. Do not mix quantities greater than 1/2 pound as dangerous heat buildup can occur causing uncontrolled decomposition of the mixed adhesive. Mixing smaller quantities will minimize the heat buildup.

Cure

Complete cure is obtained after 24 hours at 77°F. EA (Hysol) D609 will achieve handling strength after 10 minutes at 77°F (note: this can vary with different bond configurations).

Clean Up

It is important to remove excess adhesive from the work area and application equipment before it hardens. Many common solvents and citrus cleaners are suitable for removing uncured adhesive. Consult with your supplier's information pertaining to the safe and proper use of solvents.

Packaging