Selection of high-quality raw materials and fine craftsmanship, it has a simple and fast crystallization process, excellent mechanical strength, excellent processing performance and ultra-high aesthetic repair effect. Therefore, it has become the first choice for all-ceramic repair in CAD/CAM systems and is a best-seller in the world.  The digital chairside is made of all-ceramic material.

•  Easy to operate, patients can experience a convenient repair process
•  Rapid crystallization, the first choice material for immediate repair
•  High strength and non-collapse, suitable for the production of various restorations
•  Highly transparent, restores the natural color of teeth

 Transparency: HT (high transparency)/LT (low transparency)

 Color: A1/A2/A3/A3.5/A4/B1/B2/B3/B4/C1/C2/C3/C4/D2/D3/D4/BL1/BL2/BL3/BL4/OM1/OM2/OM3

 Size: C14 (18x13x15mm)

 Uniformity

 The surface of the glass ceramic block for all-ceramic dentures is smooth to the touch, uniform in color, and free of impurities and foreign matter.

 Bending strength

 The average biaxial bending strength of glass ceramics for all-ceramic dentures after complete crystallization is 637Mpa, which is higher than the strength standard value established in "GB 30367-2013 Dental Ceramic Materials". Its superior strength can be used to produce three-unit restorations containing molar areas.  body.

Indications

Veneer

Inlay

Onlay

Anterior crown

Posterior crown

Monolithic bridge (B40)

 Physical properties

 Porcelain block density (g/cm³): 2.4-2.7

 Vickers hardness (MPa): 5400+400

 Fracture toughness (MPa-m/2: 2.55

 Thermal expansion coefficient (10-6K-1): 9.8+0.5

 Crystallization temperature (C): 840-850

 Chemical solubility (ug.cm-2): 30.3

 Radioactivity (Bq/g): <0.019

 Chemical composition

 SiO₂: 61%-71%

 Li₂O: 11%-17%

 ZrO₂：1%-5%

 Other oxides: 6%-30%