Item | Specifications | |
Shrink Temperature(°C) | 110 | |
Operating Temperature Range(°C) | -55—125 | |
Tensile Strength (Mpa) | ≥10.4 | |
Ultimate Elongation (%) | ≥200 | |
Radial shrinking ratio (%) | ≥50 | |
Longitudinal Change (%) | ≤10 | |
Aging in Circulating-air Oven | 158.0±1.0°C, 168hrs | |
After Aging | Tensile Strength (Mpa) | ≥7.3 |
Ultimate Elongation (%) | ≥100 | |
Dielectric Strength at 1min, AC2500V | No breakdown | |
Volume Resistivity (Ω cm) | ≥1013 | |
Flammability | VW-1 | |
Water Absorption (%) | Less than 0.4% | |
(Copper Corrosion) | (No Corrosion) | |
Softening Point (°C) | 120±5°C | |
Tissue Strength (N/25mm) | >80 |
WE ACCEPT VISA, DISCOVER,MASTERCARD AND AMEX AND PAYPAL.
After Receiving the item, Contact Seller Within:
30 DAYS
Refund Will be Given As:
MONEY BACK
Return Shipping:
Buyer Pays for Return Shipping
20% ReStocking FEE may Apply.
AUTOMOTIVE WIRE
GXL, TXL 125 TEMP
Battery Cables.
Battery Relocation Wire kits
Tinned Copper Flat Braid
AC/DC WIRE AND SUPPLY HAS A HUGE DISTRIBUTION OF WIRE AND CABLE ALONG WITH TOP BRANDS OF ELECTRICAL PARTS FROM MANUFACTURES FROM , MOLEX, AMP, TYCO, AMPHENOL, COLEMAN CABLE, DRAKA AND MANY OTHERS.
EMAIL US THROUGH EBAY
MANUFACTURING, DISTRIBUTION ,SALES
2711 PRODUCT DR
ROCHESTER HILLS, MI 48309
After Receiving the item, Contact Seller Within:
30 DAYS
Refund Will be Given As:
MONEY BACK
Return Shipping:
Buyer Pays for Return Shipping
20% ReStocking FEE may Apply.
WE ACCEPT VISA, DISCOVER,MASTERCARD AND AMEX AND PAYPAL.
WIRE BRAID LOOM
WIRE FERRULE
CABLE LUGS
WINCH KIT CABLES
SOLAR PANEL CABLES
SOOW PORTABLE
AC/DC WIRE AND SUPPLY HAS A HUGE DISTRIBUTION OF WIRE AND CABLE ALONG WITH TOP BRANDS OF ELECTRICAL PARTS FROM MANUFACTURES FROM , MOLEX, AMP, TYCO, AMPHENOL, COLEMAN CABLE, DRAKA AND MANY OTHERS.
EMAIL US THROUGH EBAY
Item | Specifications | |
Shrink Temperature(°C) | 110 | |
Operating Temperature Range(°C) | -55—125 | |
Tensile Strength (Mpa) | ≥10.4 | |
Ultimate Elongation (%) | ≥200 | |
Radial shrinking ratio (%) | ≥50 | |
Longitudinal Change (%) | ≤10 | |
Aging in Circulating-air Oven | 158.0±1.0°C, 168hrs | |
After Aging | Tensile Strength (Mpa) | ≥7.3 |
Ultimate Elongation (%) | ≥100 | |
Dielectric Strength at 1min, AC2500V | No breakdown | |
Volume Resistivity (Ω cm) | ≥1013 | |
Flammability | VW-1 | |
Water Absorption (%) | Less than 0.4% | |
(Copper Corrosion) | (No Corrosion) | |
Softening Point (°C) | 120±5°C | |
Tissue Strength (N/25mm) | >80 |
MANUFACTURING, DISTRIBUTION ,SALES
2711 PRODUCT DR
ROCHESTER HILLS, MI 48309