MAX GPE RED A/B
OPAQUE RED
1/2 Gallon of Resin
1Quart of Curing Agent
96 Fl.Oz. Combined Volume
DESCRIPTION
MAX GPE RED A/B is a two-component epoxy based resin system, pigmented to an opaque red color. It is formulated to provide a broad range of mechanical and physical properties that are suitable for almost all types of epoxy resin applications.
MAX GPE RED A/B is mixed two parts Resin to one part Curing Agent by weight or by volume (2:1). The mixed consistency is very low in viscosity, opaque RED and easily applied by roll coat, brush or pour applied into place resulting in bubble-free castings.
It is self-leveling and has a 60 minutes gel time that allows adequate working time for casting, coating, and potting or encapsulating applications.
MAX GPE RED A/B cured coating properties exhibit very high gloss, good color stability, high surface and excellent chemical resistance.
Optimized amounts UV inhibitors, antioxidants, and stabilizers are incorporated with the MAX GPE RED A/B to provide added outdoor durability. An aliphatic polyurethane coating should be applied to further improved resistance to UV degradation.
Typical Uses and Applications
THIS KIT INCLUDES A SET OF YORKER CAPS FOR CONTROLLED DISPENSING.
Use these Yorker caps to dispense the material with ease and minimize over pouring and reduce spills. We do not recommend using
dispensing pumps. The curing agent or part B of any epoxy resin system is sensitive to moisture and carbon dioxide, which will react with the curing agent and form carbamate crystals (salt-like crystals that form on the tip of the pump) and reduce reactivity.
CARBAMATE CRYSTALS THAT FORM ON THE PUMP WHEN THE CURING AGENT IS EXPOSED AMBIENT MOISTURE AND CARBON DIOXIDE. THESE CRYSTALS ARE INSOLUBLE IN EPOXY RESIN RESULTING IN CONTAMINATION AND CAUSES POOR CURE AND AMINE-BLUSHING.
Use these Yorker caps and cut the tip to meter the orifice of the of the tip for accurate dispensing. When done, just replace the tip cap and it will exclude ambient moisture and air and keep the resin system viable for years.
Unless the kit is used continuously and within a short period of time, using dispensing pumps will cause more problems than ease-of-use. The pump leaves the bottle open to moisture (from the pressure-relief hole) and unless you plan on using the whole 2-gallon kit in less than a month, the curing agent will degrade and cause other curing problems. To use the caps, cut off the tip to the desired hole size, and attach, do not cus pass the ridgeline that keeps the tip cap in place. To dispense, lay the plastic jug unto its side and apply pressure on the bottle to dispense the contents.
When done replace the tip cap and the container is sealed and it will be usable for years.
We highly recommend using a scale to measure each component accurately.
RESIN CRYSTALLIZATION FROM PROLONGED STORAGE OR COLD WEATHER EXPOSURE
The resin component or the PART A may crystallize due to cold temperature exposure.
Please inspect the resin component for any solidified crystals which will appear as waxy solid or cloudiness on the bottom of the PART A bottle. An information postcard is included with each package.
Please cut and paste this link for more processing instructions
https://theepoxyexperts.com/coldweathernotice/
View the following video for identification and processing.
DO NOT USE UNLESS PROCESSED TO REVERT ANY CRYSTALIZED RESIN BACK TO A LIQUID STATE AND AVOID POOR CURED RESULTS.
Physical Properties
Viscosity |
900 cPs Mixed |
Mix Ratio |
100 parts A to 50 parts B by weight or volume 2:1 |
Working Time |
65 Minutes at 200 Gram Mass |
Peak Exotherm |
160oC |
Time To Reach Peak |
80 Minutes |
Density |
1.10 g/cc Cured |
Cure Time |
1 to 3 days at 25oC |
Heat Cure |
2 Hours @ 25oC Plus 1 Hour @ 120oC |
Set-To-Dry @ 10 Mil Film |
6 Hours |
Surface Dry |
9 Hours |
Handling Time |
8 Hours |
Test Criteria Room Temp Cure Room Temp + Heat Cure Hardness 78 D 81 D Izod Impact ft-lb/in .13 .19 Tensile Shear Strength psi 3,100 3,765 Tensile Strength psi 9,600 12,300 Tensile Modulus psi 460,000 489,120 Ultimate Elongation % 3.8 2.3 Heat Distortion Temperature 84oC 110oC Compressive Strength 12,300 13,000 24 Hours Water Boil % Weight Gain 2.2 1.8
Electrical Properties (1)
|
@ 23oC |
@ 40oC |
@ 60oC |
@ 100oC |
Dielectric Constant 100 Hz ASTM D-150 |
4.7 |
4.7 |
4.7 |
5.4 |
Dissipation Factor 100Hz |
3.4 x 10-3 |
3.1 x 10-3 |
3.5 x 10-3 |
6.9 x 10-3 |
Volume Resistivity Ohm-cm |
5.0 x 1015 |
3.4 x 1015 |
2.6 x 1014 |
2.4 x 1014 |
Dielectric Strength V/mil |
1/8 Inch Thick 558 |
|
|
|
BONDS TO POLYESTER OR EPOXY GEL COATS
The efficiency of the adhesion of any coating onto any substrate is highly dependent on the quality of its surface preparation. Please download our "SURFACE PREPARATION BULLETIN" to review the optimum procedure for preparing the surface for bonding or coating.
MAX GPE WHITE A/B 1.5 Gallon Kit | |
MAX GPE BLACK A/B 1.5 Gallon Kit | |
MAX GPE RED A/B 1.5 Gallon Kit | |
MAX GPE YELLOW A/B 1.5 Gallon Kit | |
MAX GPE BLUE A/B 1.5 Gallon Kit |
Use these theoretical factors to determine coverage of an unfilled epoxy resin as a theoretical guide. Please note that this is a 1.5-gallon kit and these numbers are based on theoretical physical data. It is also important to consider the type of substrate to be coated in regards to its surface roughness and porosity or absorbency,
TO DETERMINE COVERAGE ON A FLAT SMOOTH SURFACE,
DETERMINE THE LENGTH X WIDTH X THICKNESS IN INCHES
TO OBTAIN THE CUBIC VOLUME INCH OF THE MIXED RESIN NEEDED.
USE THE FOLLOWING EQUATION:
1 GALLON OF RESIN CAN COVERS 1608 SQUARE FEET
PER 1 MIL OR 0.001 INCH CURED COATING THICKNESS
(LENGTH X WIDTH X COATING THICKNESS)/ 231 CUBIC INCHES PER GALLON = CUBIC-INCHES OF COATING NEED
50 INCHES X 36 INCHES X 0.010 (10 MILS) = 18 CUBIC INCHES
18/231= .0779 GALLON OF MIXED RESIN
USE THESE FACTORS TO CONVERT GALLON NEEDED INTO VOLUMETRIC OR WEIGHT MEASUREMENTS USE THE FOLLOWING FACTORS BY THE GALLON NEEDED:
FOR EXAMPLE:
231 X .0779 = 17.99 CUBIC INCHES
OR
4195 GRAMS X .0779 = 326.79 GRAMS
FLUID GALLON VOLUME CONVERSION |
1 GALLON = 231 CUBIC INCHES= 1 GALLON = 128 OUNCES 1 GALLON = 3.7854 LITERS 1 GALLON = 4 QUARTS 1 GALLON = 16 CUPS |
FLUID GALLON MASS CONVENTIONS |
1 GALLON OF MIXED UNFILLED EPOXY RESIN = 9.23 POUNDS 1 GALLON OF MIXED UNFILLED EPOXY RESIN = 4195 GRAMS |
Pearlescent Pigments
Add these pearlescent dry pigments to the resin system to create metallic effects.
These special effects pigments are used for metallic floor coatings and art pour resin.
PEARLESCENT SILVER PEARL |
|
PEARLESCENT GOLD PEARL |
COLOR MATCHING AND COLOR BLENDING
MAX COLOR PIGMENT PASTE CONCENTRATES
These are color concentrates only and must be dispersed an epoxy resin or PART A component.
Used these colors to tint or pigment all of our MAX EPOXY RESIN SYSTEMS.
Visit the page to view addition procedure
MAX COLOR KIT https://www.ebay.com/itm/
These line of pigmented epoxy were optimized for most coating, casting, and other polymers applications.
The use of an accurate scale is highly recommended for mix accuracy and color formula repeatability.
Purchase this scale with any of our product offering and the shipping cost of the scale is free.
https://www.ebay.com/itm/222630300203
To achieve the desired tint hue and color saturation, it is best to make a small trial batch first and use a scale to accurately weigh the color concentrates as accurately as possible to achieve color reproduction when making a large batch. All color modification is done on the PART A or resin component only.
By resolute definition, a fabricated COMPOSITE material is a manufactured collection of two or more ingredients or products intentionally combined to form a new homogeneous material that is defined by its performance that should uniquely greater than the sum of its individual parts. This method is also defined as a SYNERGISTIC COMPOSITION.
COMPOSITE MATERIAL COMPOSITION
REINFORCING FABRIC & IMPREGNATING RESIN
PLUS
'ENGINEERED PROCESS'
EQUALS
COMPOSITE LAMINATE WITH THE BEST WEIGHT TO STRENGTH PERFORMANCE
With respect to the raw materials selection -fabric and resin, the fabricating process and the and curing and test validation of composite part, these aspects must be carefully considered and in the engineering phase of the composite.
TYPES OF FABRIC WEAVE STYLE AND SURFACE FINISHING
FOR RESIN TYPE COMPATIBILITY
Fabrics are generally considered ”balanced” if the breaking strength is within 15% warp to fill and are best in bias applications on lightweight structures. “Unbalanced” fabrics are excellent when a greater load is required one direction and a lesser load in the perpendicular direction.
Weaves:
Most fabrics are stronger in the warp than the fill because higher tension is placed on the warp fiber keeping it straighter during the weaving process. Rare exceptions occur when a larger, therefore stronger thread is used in the fill direction than the warp direction.
PLAIN WEAVE Is a very simple weave pattern and the most common style. The warp and fill yarns are interlaced over and under each other in alternating fashion. Plain weave provides good stability, porosity and the least yarn slippage for a given yarn count. | 8 HARNESS SATIN WEAVE The eight-harness satin is similar to the four-harness satin except that one filling yarn floats over seven warp yarns and under one. This is a very pliable weave and is used for forming over curved surfaces. | 4 HARNESS SATIN WEAVE The four-harness satin weave is more pliable than the plain weave and is easier to conform to curved surfaces typical in reinforced plastics. In this weave pattern, there is a three by one interfacing where a filling yarn floats over three warp yarns and under one. | 2x2 TWILL WEAVE Twill weave is more pliable than the plain weave and has better drivability while maintaining more fabric stability than a four or eight harness satin weave. The weave pattern is characterized by a diagonal rib created by one warp yarn floating over at least two filling yarns. |
![]() | ![]() | ![]() | ![]() |
All of the fiberglass fabrics is woven By HEXCEL COMPOSITES, a leading manufacturer of composite materials engineered for high-performance applications in marine, aerospace for commercial and military, automotive, sporting goods and other application-critical performance. These fabrics are 100% epoxy-compatible and will yield the best mechanical properties when properly fabricated.
Finishing Cross Reference And Resin Type Compatibility
RESIN COMPATIBILITY | Industries | Clark Schwebel | J.P Stevens | Uniglass Industries |
Epoxy, Polyester | VOLAN A | VOLAN A | VOLAN A | VOLAN A |
Epoxy, Polyester | I-550 | CS-550 | S-550 | UM-550 |
Phenolic, Melamine | I-588 | A1100 | A1100 | A1100 |
Epoxy, Polyimide | I-589 | Z6040 | S-920 | UM-675 |
Epoxy | I-399 | CS-272A | S-935 | UM-702 |
Epoxy | | CS-307 | | UM-718 |
Epoxy | | CS-344 | | UM-724 |
Silicone | 112 | 112 | | n-pH (neutral pH) |
AVAILABLE FIBERGLASS, CARBON FIBER, AND KEVLAR FABRICS
HEXCEL 120 1.5-OUNCE FIBERGLASS PLAIN WEAVE 5 YARDS | |
HEXCEL 120 1.5-OUNCE FIBERGLASS PLAIN WEAVE 10 YARDS | |
HEXCEL 7532 7-OUNCE FIBERGLASS PLAIN WEAVE 5 YARDS | |
HEXCEL 7500 10 OUNCE FIBERGLASS PLAIN WEAVE 3 YARDS | |
HEXCEL 7500 10 OUNCE FIBERGLASS PLAIN WEAVE 5 YARDS | |
HEXCEL 3582 14 OUNCE FIBERGLASS SATIN WEAVE 5 YARDS | |
HEXCEL 3582 14 OUNCE FIBERGLASS SATIN WEAVE 10 YARDS | |
HEXCEL 1584 26 OUNCE FIBERGLASS SATIN WEAVE 3 YARDS | |
HEXCEL 1584 26 OUNCE FIBERGLASS SATIN WEAVE 5 YARDS | |
FIBERGLASS 45+/45- DOUBLE BIAS 3 YARDS | |
|
|
CARBON FIBER FABRIC 3K 2x2 TWILL WEAVE 6 OZ. 3 YARDS | |
CARBON FIBER FABRIC 3K PLAIN WEAVE 6 OZ 3 YARDS | |
|
|
KEVLAR 49 HEXCEL 351 PLAIN WEAVE FABRIC 2.2 OZ |
How To Mix Epoxy Resin For Food Contact Coating. Avoid Tacky Spots, Minimize Air Bubble When Mixing - YouTube
Video will open in a new window
Using the eBay App? Paste link into a browser window:
MAX BOND LOW VISCOSITY A/B
Marine Grade
MAX BOND LOW VISCOSITY 32-Ounce kit | |
MAX BOND LOW VISCOSITY 64-Ounce Kit | |
MAX BOND LOW VISCOSITY 1-Gallon Kit | |
MAX BOND LOW VISCOSITY 2-Gallon kit | |
MAX BOND LOW VISCOSITY 10-Gallon Kit |
MAX 1618 A/B
Crystal Clear, High Strength, Lowest Viscosity (Thin), Durability & Toughness, Excellent Wood Working Resin
MAX 1618 A/B 48-Ounce Kit | |
MAX 1618 A/B 3/4-Gallon Kit | |
MAX 1618 A/B 3/4-Gallon Kit | |
MAX 1618 A/B 1.5-Gallon Kit |
MAX CLR A/B
Water Clear Transparency, Chemical Resistance, FDA Compliant For Food Contact, High Impact, Low Viscosity
MAX CLR A/B 24-Ounce Kit | |
MAX CLR A/B 48-Ounce Kit | |
MAX CLR A/B 96-Ounce Kit | |
MAX CLR A/B 96-Ounce Kit | |
MAX CLR A/B 1.5-Gallon Kit |
MAX GRE A/B
GASOLINE RESISTANT EPOXY RESIN
Resistant To Gasoline/E85 Blend, Acids & Bases, Sealing, Coating, Impregnating Resin
MAX GRE A/B 48-Ounce Kit | |
MAX GRE A/B 96-Ounce Kit |
MAX HTE A/B
HIGH-TEMPERATURE EPOXY
Heat Cured Resin System For Temperature Resistant Bonding, Electronic Potting, Coating, Bonding
MAX HTE A/B 80-Ounce Kit | |
MAX HTE A/B 40-Ounce Kit |
Step Three:
Proper Lay-Up Technique -Putting It All Together
Pre-lay-up notes
Mix the proper amount of resin needed and be accurate proportioning the resin and curing agent. Adding more curing agent than the recommended mix ratio will not promote a faster cure. Over saturation or starving the fiberglass or any composite fabric will yield poor mechanical performance. When mechanical load or pressure is applied to the composite laminate, the physical strength of the fabric should bear the stress and not the resin. If the laminate is over saturated with the resin it will most likely to fracture or shatter instead of rebounding and resist damage.
Don’t how much resin to use to go with the fiberglass?
A good rule of thumb is to maintain a minimum of 30 to 35% resin content by weight, this is the optimum ratio used in high-performance prepreg (or pre-impregnated fabrics) typically used in aerospace and high-performance structural application.
For general hand lay-ups, calculate using 60% fabric weight to 40% resin weight as a safety factor. This will ensure that the fabricated laminate will be below 40% resin content depending on the waste factor accrued during fabrication.
Place the entire pre-cut fiberglass to be used on a digital scale to determine the fabric to resin weight ratio. Measuring by weight will ensure accurate composite fabrication and repeatability, rather than using OSY data.
THE USE OF A WEIGHING SCALE IS HIGHLY RECOMMENDED
Purchase this scale with any of our product offering and the shipping cost of the scale is free.
https://www.ebay.com/itm/222630300203
A good rule of thumb is to maintain a minimum of 30 to 35% resin content by weight, this is the optimum ratio used in high-performance prepreg (or pre-impregnated fabrics) typically used in aerospace and high-performance structural application. For general hand lay-ups, calculate using 60% fabric weight to 40% resin weight as a safety factor. This will ensure that the fabricated laminate will be below 40% resin content depending on the waste factor accrued during fabrication.
Place the entire pre-cut fiberglass to be used on a digital scale to determine the fabric to resin weight ratio. Measuring by weight will ensure accurate composite fabrication and repeatability, rather than using OSY data.
Typical fabric weight regardless of weave pattern
1 ounce per square yard is equal to 28.35 grams
1 square yard equals to 1296 square inches (36 inches x 36 inches)
FOR EXAMPLE
1 yard of 8-ounces per square yard (OSY) fabric weighs 226 grams
1 yard of 10-ounces per square yard (OSY) fabric weighs 283 grams
Ounces per square yard or OSY is also known as aerial weight, which is the most common unit of measurement for composite fabrics. To determine how much resin is needed to adequately impregnate the fiberglass, use the following equation:
(Total Weight of Fabric divided by 60%)X( 40%)= weight of mixed resin needed
OR
fw= fabric weight
rc= target resin content
rn=resin needed
MASTER EQUATION
(fw/60%)x(40%)=rn
FOR EXAMPLE
1 SQUARE YARD OF 8-OSY FIBERGLASS FABRIC WEIGHS 226 GRAMS
(226 grams of dry fiberglass / 60%) X 40% = 150.66 grams of resin needed
So for every square yard of 8-ounce fabric, it will need 150.66 grams of mixed resin.
Computing For Resin And Curing Agent Amount
150.66 grams of resin needed
MIX RATIO OF RESIN SYSTEM IS 2:1 OR
50 PHR (per hundred resin)
2 = 66.67% (2/3)
+
1 = 33.33%(1/3)
=
(2+1)=3 or (66.67%+33.33%)=100% or (2/3+1/3)= 3/3
150.66 x 66.67%= 100.45 grams of Part A RESIN
150.66 x 33.33%= 50.21 grams of Part B CURING AGENT
100.45 + 50.21 = 150.66 A/B MIXTURE
GENERAL LAY-UP PROCEDURE
Apply the mixed resin onto the surface and then lay the fabric and allow the resin to saturate through the fabric.
NOT THE OTHER WAY AROUND
This is one of the most common processing error that yields sub-standard laminates. By laying the fiberglass onto a layer of the prepared resin, fewer air bubbles are entrapped during the wetting-out stage. Air is pushed up and outwards instead of forcing the resin through the fabric which will entrap air bubbles. This technique will displace air pockets unhindered and uniformly disperse the impregnating resin throughout the fiberglass.
HAND LAY-UP TECHNIQUE
Eliminating air entrapment or void porosity in an epoxy/fiberglass lay-up process
Similar to the Vacuum Bagging Process where the negative pressure is used to apply consolidation force to the laminate while the resin cures, the resin is infused into the fabric lay-up by sucking the impregnating resin and thus forming the composite laminate.
The VARTM Process produces parts that require less secondary steps, such as trimming, polishing or grinding with excellent mechanical properties. However, the vacuum infusion requires more additional or supplemental related equipment and expendable materials. So the pros and cons of each presented composite fabrication process should be carefully determined to suit the user's capabilities and needs.
Please view the following video demonstration which explains the process of Vacuum Infusion or VARTM process.
ULTIMATE COMPRESSIVE STRENGTH
6500 pounds to failure / 0.498 square inch = 13,052 psi max compressive strength
Other mechanical and physical test should be used to determine other aspect of performance. Here is a link to a technical journal that discusses the importance of validation and testing of composite materials.
Please cut and paste the following link to review the journal.
https://nopr.niscair.res.in/bitstream/123456789/20966/1/IJEMS%2020(4)%20299-309.pdf
**********************************************
DON'T FORGET OUR EPOXY MIXING KIT
Click The Link to add to order
https://www.ebay.com/itm/222623932456
EVERYTHING YOU NEED TO MEASURE, MIX, DISPENSE OR APPLY ANY OF OUR
Your purchase constitutes the acceptance of this disclaimer. Please review before purchasing this product. The user should thoroughly test any proposed use of this product and independently conclude satisfactory performance in the application. Likewise, if the manner in which this product is used requires government approval or clearance, the user must obtain said approval. The information contained herein is based on data believed to be accurate at the time of publication. Data and parameters cited have been obtained through published information, PolymerProducts laboratories using materials under controlled conditions. Data of this type should not be used for a specification for fabrication and design. It is the user's responsibility to determine this Composites fitness for use. There is no warranty of merchantability of fitness for use, nor any other express implied warranty. The user's exclusive remedy and the manufacturer's liability are limited to refund of the purchase price or replacement of the product within the agreed warranty period. PolymerProducts and its direct representative will not be liable for incidental or consequential damages of any kind. Determination of the suitability of any kind of information or product for the use contemplated by the user, the manner of that use and whether there is any infringement of patents is the sole liability of the user.