Specifications:
Material Mark:N52
Base Material: Intermetallic Compound Nd2Fe14B
Size: Approx.8*3mm / 0.31*0.12inches
Coercivity:1009（KA/m）
Remanence:11.9-12.5（T）
Intrinsic Coercive Field:13（KA/m）
Maximum Energy Product:34-39.5（KJ/m3）
Density:7.5（g/cm3）
Working Temperature: 80-220（℃）
The Curie Temperature: 0-80（℃）
Widly Use in: Electronic products, mobile phones, laptops, digital cameras, motor, electrical appliances, antenna chuck, electronic toys, gifts, packaging, leather goods, luggage, handbags, furniture hardware and other industries.
Features:
1.Hard texture, stable performance, high corrosion resistance.
2.High temperature resistance, the working temperature can be up to 200 degrees Celsius.
3.The maximum magnetic energy product (BHmax) is 10 times higher than Ferrite.
4.With extremely high magnetic energy product and coercivity, it can lift a weight 640 times its own weight.
5.Widely used in modern industry and electronic technology, drive to achieve miniaturize, lightweight and thin equipment.
Note:
*If the working temperature is higher than the bearing temperature of the magnet, the magnet will be demagnetized slowly until there is no magnetism.
*Magnets should be stored in a dry, constant temperature environment, separated and wrapped in plastic, wood, cardboard, foam, etc. Keep away from iron and easily magnetized objects.Such as monitors, computers, televisions, mobile phones and so on.
*Take and put lightly, storage should keep the environment dry, do not pile directly on the ground.
*When the magnets are inseparable from each other, it is recommended to push stagger horizontally, must not pull or pry hardly. Do not immediately put the removed magnet back into the magnet pile. Isolate the magnet immediately.
*Due to the lighting and screen settings, the real color may slightly different from the picture.
*Please allow slight size differences due to different manual measurement.
Package Includes:
1-100pcs Neodymium Disc NdFeB Magnets
(Others are NOT included)