KLUBER KLUBERPASTE HEL 46-450 CHEAPEST ON THE MARKET SUGGESTED DISTRIBUTION PRICE IS £475.00 PER 750g
Screw paste for conventional and high-alloy steels (Cr-Ni steels) up to 1000 °C. Lubricating and assembly paste for connections in hot air ducts (e.g. automotive exhaust systems). For connecting elements in turbochargers and compressors. The test was performed acc. to VW-TL 52112 Bolt: DIN 931-2; Material:1.4989; Nut, material: 1.4923. The nuts were preloaded with 70 Nm and stored at 750 °C for 100 hours. After this period a low release torque was measured.
Klüberpaste HEL 46-450 is a black hot screw paste for highalloy steels. It contains fully synthetic polyalkylene glycol and ester base oils and a combination of inorganic solid lubricants. Klüberpaste HEL 46-450 is suitable for a temperature range between -40 °C and 1000 °C. In the normal temperature range (i.e. below 200 °C) it shows good anticorrosion behaviour and good water resistance. Above 200 °C it acts as a dry lubricant.
| Product specifications : | Klüber Klüberpaste HEL 46-450 | |
| Article number | 089032 | |
| Lower service temperature | -40 °C / -40 °F | |
| Upper service temperature | 1000 °C / 1832 °F | |
| Colour space | black | |
| Density at 20 °C | approx. 1.43 g/cm³ | |
| Worked penetration, 25 °C, lower limit value | DIN ISO 2137 | 325 x 0.1 mm |
| Worked penetration, 25 °C, upper limit value | DIN ISO 2137 | 340 x 0.1 mm |
| Corrosion inhibiting properties of lubricating greases, (SKF-EMCOR), test duration: 1 week, distilled water | DIN 51802 | <= 1 corrosion degree |
| Flow pressure of lubricating greases, test temperature: -35 °C | DIN 51805-2 | <= 600 mbar |
| Drop point, | DIN ISO 2176, IP 396 | >= 250 °C |
| Four-ball tester, welding load, | DIN 51350 pt. 04 | >= 5 000 N |
| High-temperature screw test according to VW-TL 52112, breakaway torque | <= 120 Nm | |
| Friction coefficient screw test, measured with hexagon bolts M10x30-8.8, tightening speed n = 5 rpm, number of screws = 20, nut M10-8, plain and degreased, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 50 Nm, averaged bearing surface friction coefficient (initial tightening) | DIN EN ISO 4017 | 0.11 |
| Friction coefficient screw test, measured with hexagon bolts M10x30-8.8, tightening speed n = 5 rpm, number of screws = 20, nut M10-8, plain and degreased, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 50 Nm, standard deviation (S) of averaged bearing surface friction coefficient (initial tightening) | DIN EN ISO 4017 | 0.015 |
| Friction coefficients screw test, screw M 10x30-8.8, black and nut M 10-8, DIN EN ISO 4032, polished, averaged thread friction coefficient (first-time tightening) | DIN EN ISO 4017 | 0.09 |
| Friction coefficient screw test, Measured with hexagon bolts M10x30-8.8, tightening speed n = 5 rpm, number of screws = 20, nut M10-8, plain and degreased, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 50 Nm, standard deviation (S) of averaged thread friction coefficient (initial tightening) | DIN EN ISO 4017 | 0.01 |
| Friction coefficient screw test, measured with hexagon bolts M10x50-A2-70, tightening speed n = 5 rpm, number of screws = 20, material of the nut A2, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 40 Nm, averaged bearing surface friction coefficient (initial tightening) | DIN EN ISO 4017 | 0.09 |
| Friction coefficient screw test, measured with hexagon bolts M10x50-A2-70, tightening speed n = 5 rpm, number of screws = 20, material of the nut A2, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 40 Nm, standard deviation (S) of averaged bearing surface friction coefficient (initial tightening) | DIN EN ISO 4017 | 0.006 |
| Friction coefficient screw test, measured with hexagon bolts M10x50-A2-70, tightening speed n = 5 rpm, number of screws = 20, material of the nut A2, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 40 Nm, averaged thread friction coefficient (initial tightening) | DIN EN ISO 4017 | 0.11 |
| Friction coefficient screw test, measured with hexagon bolts M10x50-A2-70, tightening speed n = 5 rpm, number of screws = 20, material of the nut A2, face material 42CrMo4 with roughness Ra 1.6, tightening torque MA = 40 Nm, standard deviation (S) of averaged thread friction coefficient (initial tightening) | DIN EN ISO 4017 | 0.03 |
| Water resistance, 3 h/90 °C, rating | DIN 51807 pt. 01 | <= 1 - 90 |
| Minimum shelf life from the date of manufacture - in a dry, frost-free place and in the unopened original container, approx. | 24 months |
It is important to clean and degrease the contact surfaces thoroughly before applying Klüberpaste HEL 46-450. A thin layer of paste is then applied by brush, leather cloth or plastic sponge. Klüberpaste HEL 46-450 spreads easily over the entire surface and thus prevents excess lubrication. Close container immediately after use in order to prevent contamination. The friction values indicated on page 2 in the Section Product Data were determined with two different materials. Other materials/surfaces have to be checked accordingly.